furnace brick lining

基本解释

Since the SiC brick was applied , the life of taphole and lining on the furnace was prolonged .
应用碳化硅砖后，延长了出铁口及整个炉衬的使用寿命。
To prolong furnace lining′s service life, refining furnace lining is rammed with magnesia ramming material instead of magnesia brick.
为延长炉衬的使用寿命，用镁质捣打料代替镁砖打结精炼电炉炉衬。
Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied.
采用光学显微镜（OM）、扫描电镜（SEM）和能谱仪（E DAX）对AOD炉用镁钙砖的残砖进行了分析，探讨了炉衬镁钙砖的侵蚀机理。