基本解释

• [能源科学技术]晶间应力腐蚀开裂晶间应力腐蚀裂缝

英汉例句

双语例句

• The corrosion behavior of 2D12 alloy was evaluated including intergranular corrosion, exfoliation and stress corrosion cracking.
  对不同规格2D12铝合金进行晶间腐蚀、剥蚀和应力腐蚀性能测定。
• The cracking of alloy with very low stress-corrosion resistance, welded and stored in open air for a long time, is caused by the welded stress and such a fracture is a typical intergranular fracture.
  抗应力腐蚀性能低的合金焊接后，在大气中长期存放沿熔合线发生的开裂，是由焊接应力引起的，断口是典型的脆性沿晶断裂。

专业释义

能源科学技术

• 晶间应力腐蚀开裂
• 晶间应力腐蚀裂缝